OK Autrod 4047 1,2 (OK 18.05) [1805129870] |
OK Autrod 4047
GMAW
OK Autrod 4047 was originally developed as a brazing alloy to take advantage of its low melting point and narrow freezing range. In addition, it has a higher silicon content than OK Autrod 4043, which provides increased fluidity and reduced shrinkage. The alloy produces bright, almost smut-free welds. Hot cracking is significantly reduced when using OK Autrod 4047 as a filler alloy. The alloy can be used in applications with sustained elevated temperatures. Non-heat treatable.
Welding current
DC(+)
Classifications |
Approvals |
Typical all weld metal composition, % |
Typical mech. properties all weld metal |
SFA/AWS A5.10 |
ER4047 |
EN ISO 18273 |
S Al 4047 (AlSi12) |
|
CWB |
AWS A5.10 (Item number ending with A) |
|
|
|
Si |
12,0 |
Mn |
<0,15 |
Cu |
<0,05 |
Ti |
<0,15 |
Zn |
<0,20 |
Fe |
<0,6 |
Wire composition |
|
Yield stress, MPa
80
Tensile strength, MPa
170
Elongation, %
12
Elongation, %
12 |
|
Diameter, mm |
0,9 |
1,2 |
1,6 |
Arc voltage, V |
13-24 |
20-29 |
25-30 |
Welding current, A |
60-170 |
140-260 |
190-350 |
Wire feed, m/min |
- |
6-13 |
4,5-7,5 |
Deposition rate kg weld metal/hour |
- |
1,1-2,4 |
1,5-2,5 |
| | | |